The glass fibre filters from LABSOLUTE® are made of borosilicate glass without binder and are thus biologically inert. The filters provide a high retention power and simultaneously enable elevated flow rates, which makes them applicable for almost every area of laboratory filtration. Among other things, they are used for clarification of protein solutions, air or water monitoring and for gravimetric and waste water analyses. Furthermore, they can be ideally used as prefilters for membranes.

• Very high resistance to almost all kinds of chemicals
• Temperature-resistant up to 500 °C
• Autoclavable up to 134 °C

• Thickness: 0.26 mm
• Weight: 52 g/m²

The glass fibre filters from LABSOLUTE® are made of borosilicate glass without binder and are thus biologically inert. The filters provide a high retention power and simultaneously enable elevated flow rates, which makes them applicable for almost every area of laboratory filtration. Among other things, they are used for clarification of protein solutions, air or water monitoring and for gravimetric and waste water analyses. Furthermore, they can be ideally used as prefilters for membranes.

• Very high resistance to almost all kinds of chemicals
• Temperature-resistant up to 500 °C
• Autoclavable up to 134 °C

• Thickness: 0.26 mm
• Weight: 53 g/m²

The glass fibre filters from LABSOLUTE® are made of borosilicate glass without binder and are thus biologically inert. The filters provide a high retention power and simultaneously enable elevated flow rates, which makes them applicable for almost every area of laboratory filtration. Among other things, they are used for clarification of protein solutions, air or water monitoring and for gravimetric and waste water analyses. Furthermore, they can be ideally used as prefilters for membranes.

• Very high resistance to almost all kinds of chemicals
• Temperature-resistant up to 500 °C
• Autoclavable up to 134 °C

• Thickness: 0.45 mm
• Weight: 75 g/m²

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured from high grade borosilicate glass. They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C. Filtration velocity acc. to Herzberg.

Wide range of applications including:

• Retention of fine analytical precipitates
• Retention of biochemical gelatinous precipitates
• Water/air pollution analyses
• As prefilters for membranes
• Scintillation counting
• Radioimmunoassay

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
Extremely efficient filter made to retain fine particles and micro organisms. Particle retention to 1.2 µm.

The general purpose high efficiency glass microfibre filter. Particle retention to 1.6 µm.

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
This ultra-fine filter has a 98 % retention efficiency for particles as small as 0.7 µm in liquids. Particle retention to 0.7 µm.

Suitable for analytical and gravimetric analyses, as well as a pre-filter.

• Hydrophilic
• Liquid Filtration
• Non-sterile

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
Circles. High retention at high flow rates. Widely used in water pollution monitoring techniques for suspended solids, and is specified in US Method 934-AH. Particle retention to 1.5µm.

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
Thick filter made from less fibres and retaining around 3µm particles with a very high loading capacity. Extremely high speed. Particle retention to 2.7µm.

Recommended filters for controlling both air and water pollution.

• Made of 100 % borosilicate glass fibres without binders
• Extremely low content in alkali-earth metals
• Chemical stability: It keeps all its properties in contact with acid solutions (except hydrofluoric acid) and basic solutions at moderate concentrations
• Usable as a pre-filter for membranes to prevent the membranes from silting up
• Deposition of (radioactive) aerosols and monitoring of nuclear power plants
• Gravimetrical analysis of organic and inorganic impurities in water and waste water according to DIN 38409 and EN 872 (suspended particles)
• Measurement of immission, measurement of dust in air and gases, monitoring of the efficiency of filtration and dedusting, monitoring the combustion air of power plants and of the steel and iron industry
• Measurement of dust release in workplace and production processes and the purification of compartment air
• Stability at high temperatures: It keeps its properties up to 500 °C
• High flow speed and high permeability to air

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
To Herzberg.

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
Manufactured from quartz microfibre to withstand high temperatures. Can be used up to 500 °C.

Can be used up to a maximum of 200 °C. With organic binder.

Recommended filters for environmental analysis and controlling both air and water pollution.

• Made of 100 % borosilicate glass fibres with binders
• Glass fibre filters capture fine particles down to 1 µm from liquids, in air, gases and aerosols with even 0.3 to 0.5 µm being absorbed
• Extremely low content in alkali-earth metals
• Chemical stability: It keeps all its properties in contact with acid solutions (except hydrofluoric acid) and basic solutions at moderate concentrations
• Stabile at temperatures up to 500 °C
• Gravimetrical analysis of organic and inorganic impurities in water and waste water according to DIN 38409 and EN 872 (suspended particles)
• Measurement of immission, measurement of dust in air and gases, monitoring of the efficiency of filtration and dedusting, monitoring the combustion air of power plants and of the steel and iron industry
• Measurement of dust release in workplace and production processes and the purification of compartment air
• Measurement of scintillation

Glass microfibre filters have a fast filtration and a high loading capacity and particle retention rate. Manufactured without chemical binder from high grade borosilicate glass. (Exception: GF6, GF9). They are suitable for gravity or low suction filtration. Filtration speeds generally very much higher than conventional cellulose papers. Efficient retention of micron size particles. Must be used flat. Ideal for use in flat perforated plate Buchner type funnels (not sintered glass models). Can be used up to 500 °C.
Extremely efficient filter made to retain fine particles and micro organisms. Particle retention to 1.2 µm.

With acrylic latex binder (4% to 6%, determined by ashing).

This binder free paper offers fine particle retention, high flow rate and good loading capacity. it is used for high efficiency laboratory filtration as well as air sampling. This filter is stable up to +500 °C.