The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2020, medium to slow filtering, particle retention 5-13 µm, filtration speed 88 s according to DIN 53137, basis weight 73 g/m², thickness 0.16 mm

For fast filtration with fine particles for general, electrolytic application in schools, research, health care, food and cosmetics industry.

The LABSOLUTE® filter crucibles are made of borosilicate glass 3.3 and are therefore extremely resistant against high temperatures and chemicals. The crucibles are autoclavable and can be perfectly used for applications in qualitative analysis and preparative chemistry. The sintered glass filter disc has a porosity of 4 which equals a pore size of 5 -15 µm.

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2015, medium to slow filtering, particle retention 5-8 µm, filtration speed 50 s according to DIN 53137, basis weight 87 g/m², thickness 0.16 mm

For fast filtration with fine particles, when the filtration speed plays a minor role.

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2020, medium to slow filtering, particle retention 5-13 µm, filtration speed 88 s according to DIN 53137, basis weight 73 g/m², thickness 0.16 mm

For fast filtration with fine particles for general, electrolytic application in schools, research, health care, food and cosmetics industry.

The wet-strengthened filter papers exhibit a very high degree of mechanical stability. They are resistant against acidic and alkaline solutions and are suitable for pressure and vacuum filtration. The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2105, fast filtering, particle retention 12-15 µm, filtration speed 10 s according to DIN 53137, basis weight 84 g/m², thickness 0.20 mm, wet strengthened

For large-volume or gel-like deposits (e.g. hydroxides of iron and copper or sulphides of iron and cobalt). Especially high mechanical strength and resistance to acids and alkalis.

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2005, fast filtering, particle retention 12-15 µm, filtration speed 10 s complies with DIN 53137, basis weight 84 g/m², thickness 0.20 mm

For large-volume or gel-like deposits (e.g. hydroxides of iron and copper or sulphides of iron and cobalt).

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2010, medium fast filtering, particle retention 8-12 µm, filtration speed 20 s according to DIN 53137, basis weight 84 g/m², thickness 0.17 mm

The most frequently used filter for analytical work, e.g. malt analyses according to EBC, precipitation of silver sulphide, precipitation of chromates (iron, lead, arsenic).

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2015, medium to slow filtering, particle retention 5-8 µm, filtration speed 50 s according to DIN 53137, basis weight 87 g/m², thickness 0.16 mm

For fast filtration with fine particles, when the filtration speed plays a minor role.

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2005, fast filtering, particle retention 12-15 µm, filtration speed 10 s according to DIN 53137, basis weight 84 g/m², thickness 0.20 mm

For large-volume or gel-like deposits (e.g. hydroxides of iron and copper or sulphides of iron and cobalt).

The qualitative filter papers are manufactured from pure cellulose with a proportion of alpha-cellulose of almost 100 %. The ash content is about 0.06 %.

Grade 2025, slow filtering, particle retention 3-5 µm, filtration speed 100 s according to DIN 53137, basis weight 84 g/m², thickness 0.15 mm

For precipitation such as zinc, nickel and tin sulphide, calcium fluoride and calcium hydroxide.